Rogers 4003 PCB
Name: Rogers 4003 PCB
Material: Rogers 4003 material
rogers 4003 dielectric constant: 3.38
Layer: 4003+4450F
rogers 4003 thickness: 0.508mm(20mil)
Finished Thickness: 2.0mm
Rogers 4003 substrate Copper Thickness: 17μm
Finished Copper Thickness: 1OZ
SurfaceTreatment: Immersion Gold
Color:Green /White
Min Trace / Space: 6mil/6mil
Features: Rogers PCB, tg280 high temperature resistant PCB
RO4003C laminates are available in a variety of configurations in 1080 and 1674 glass fabric styles, all conforming to the same laminate electrical performance specifications. RO4003C laminates offer tightly controlled dielectric constant (Dk) and low loss while using the same processing methods as standard epoxy/glass, but at a fraction of the cost of traditional microwave laminates. Unlike PTFE-based microwave materials, no special through-hole processing or handling procedures are required.
RO4003C material is bromine free and does not meet UL 94 V-0 ratings. For applications or designs that require a UL 94 V-0 flammability rating, RO4835™ and RO4350B™ laminates do meet this requirement.
feature
Dk is 3.38 +/- 0.05
Dissipation factor 0.0027 at 10 GHz
Low Z-axis thermal expansion coefficient at 46 ppm/°C
Name: Rogers 4003 PCB
Material: Rogers 4003 material
rogers 4003 dielectric constant: 3.38
Layer: 4003+4450F
rogers 4003 thickness: 0.508mm(20mil)
Finished Thickness: 2.0mm
Rogers 4003 substrate Copper Thickness: 17μm
Finished Copper Thickness: 1OZ
SurfaceTreatment: Immersion Gold
Color:Green /White
Min Trace / Space: 6mil/6mil
Features: Rogers PCB, tg280 high temperature resistant PCB